Description
PSI Quick Repair Paste steels
Polymeric Systems Inc. patent product cost, and daub sticks with the same core, in lien with performance of the pasted objects, in allusion to paste steels with similar gravity, density and expansion coefficient, to guarantee the quality of viscidity.
Varity and applicable parts
( FASTSTEEL )
Paste Steel
Used for repairing steel products, such as repairing crack in engine cylinder body, filling foundry sand hole, sealing leakage piping, restoring defect parts and making samples.
( REPAIRITQUIK )
Repair It Quick
Multi-purpose, quick solidifying, initially solidifying duration of 3~5 minutes, able to paste metal, wood, glass, ceram and other materials, and capable of sealing the electric insulation.
( AQUAREPAIR )
Aqua Repair
Excellent in comprehensive performance, able to repair and fix under water; in particular, applicable in sealing of leakage in glass steel hull, bathtub and PVC pipe, outstanding in aging-resistant performance
( QUICKCOPPER )
Quick Copper
Able to repair leakage problems in pipes, valve, spout, tap and radiator even under the condition of humid surfaces.
( QUIKALUMINUM )
Quick Aluminum
Able to repair and repair aluminum and aluminum alloy, vessel, casting and doors and windows.
Usage
Eliminating dirt, oil soil and other deposit builders on the parts to be pasted, taking paste steel from the plastic pipe, cutting the needed amount, mixing the different colors inside and outside the pipe, pasting on and then taking it away from the surface of the parts to be pasted so as to improve the adherence, and dipping some water with fingers to nap it in order to achieve a smoother surface. The mixed paste could react in a short time and becomes warmer in 3-5 minutes and solidified in 5-25 minutes for the intensity and rigidity of the polishing and processing. In winter, in cold areas, when it is used, it should be heated to or above the room temperature and then used for repairing surfaces.
Technical Coefficient of Quick Repairs
Materials
|
|
Repair it quick |
Aqua repair |
|
|
High- temperature healant | |||
Name |
Unit |
Test Standard |
|
|
|
|
|
| |
Operation agglutinate duration |
Minute |
|
3 - 5 |
3 - 5 |
20 - 30 |
3 - 5 |
6 - 8 |
1 - 2 | |
2 24-hr solidifying rigidity |
Shaw |
ASTM |
75-85 |
70-80 |
65-75 |
75-85 |
60-70 |
75-80 | |
Adhesive stretch intensity |
Mpa |
ASTM |
5.5-6.9 |
5.5-6.9 |
5.5-6.9 |
4.1-5.5 |
3.5-5.6 |
51 | |
Compression strength |
Mpa |
ASTM D695 |
69-97 |
69-97 |
69-97 |
69-97 |
69-97 |
84 | |
Temperature-proof limitation |
|
|
121 (continuous) 149 (interim) |
-10-260 | |||||
Chemical resistant performance |
|
U1698 |
Anti-grease, alcohol, ketone, hydrocarbon, salting liquid, acid and alkali | ||||||
Rate of shrinkage |
|
|
1% | ||||||
Surface resistance |
M |
ASTM D257 |
30 , 000 | ||||||
Insulation intensity |
KV/mm |
ASTMD149 |
11.8 | ||||||
Non-volatile matter |
|
|
100% | ||||||
Shelf life |
Normal temperature |
|
The best shelf life is 12 months and it could be used within 3-5 years. |
2-3 2-3 years | |||||
Features